Blend Polyol SDA13E Spray Rigid PU Foam For Cold storage DESCRIPTION SDA13E cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following: - The strong adhesive force, convenient construction and no seams.
- The low thermal conductivity, low water absorption and good dimensional stability.
- The long service life.
TYPICAL PHYSICAL PROPERTIES Physical Properities | Test Method | Metric | Value |
Core Density | GB/T 6343-2009 | kg/m3 | 45.3 |
Compressive Strength | GB/T 8813-2008 | kPa | 264 |
Tensile Strenght | GB/T 9641-88 | kPa | 136 |
Oxygen index | GB/T 2406.2-2009 | % | 23.4 |
Initial Thermal Conductivity | GB/T 10294-2008 | W/(m·K) | 0.022 |
Close Cell Content | GB/T 10799-2008 | % | ≥88 |
Water Absorption | GB/T 8810-2005 | % | ≤3 |
Dimensional Stability (Foam made After 6 days) | -25ºC | GB/T 8811-2008 | % | ≤±1 ≤±1 |
70ºC |
Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.Other unmentioned matters and TDS&MSDS.Please visit our official website www.shundapu.com
Or please contact us for information:
Tel: +86 535 6739386.
------------------------------------------------------------------
DESCRIPTION SD1133 cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following: - The strong adhesive force, convenient construction and no seams.
- The low thermal conductivity, low water absorption and good dimensional stability.
- The long service life.
TYPICAL PHYSICAL PROPERTIES Physical Properities | Test Method | Metric | Value |
Core Density | GB/T 6343-2009 | kg/m3 | 45.3 |
Compressive Strength | GB/T 8813-2008 | kPa | 264 |
Tensile Strenght | GB/T 9641-88 | kPa | 136 |
Oxygen index | GB/T 2406.2-2009 | % | 23.4 |
Initial Thermal Conductivity | GB/T 10294-2008 | W/(m·K) | 0.022 |
Close Cell Content | GB/T 10799-2008 | % | ≥88 |
Water Absorption | GB/T 8810-2005 | % | ≤3 |
Dimensional Stability (Foam made After 6 days) | -25ºC | GB/T 8811-2008 | % | ≤±1 ≤±1 |
70ºC |
Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.
COMPONENT PRODUCT SPECIFICATIONS Property | Blend polyol SD1133 | Polymeric MDI Pm200 |
Appearance | Pale yellow liquid. | Brown liquid |
Specific gravity at 25°C | 1.10±0.10 g/cm3 | 1.22-1.25 g/cm3 |
Viscosity at 25°C | 300±100 cps | 200±50 cps |
Shelf life | 3 months | 12 months |
REACTIVITY PROFILE Cream Time | Gel Time | Rise Time |
0-1 s | 2-3 s | 4-6 s |
INSTALLATION GUIDELINE SD1133 | Ambient Temperatures | Spraying Temperatures | Minimum Spray Pressures |
Summer | 10-35ºC | 35-41ºC | 5516kPa (800 psi) |
Sping~Autumn | 0-15ºC | 35-45ºC | 5516kPa (800 psi) |
Winter | -10-5ºC | 35-50ºC | 5516kPa (800 psi) |
SD1133:PM200=1:1(volume ratio)
Foaming Machine:Polyurethane Rigid foam Spray Machine
ADDITIONAL INFORMATION - Maximum per pass thickness is 35mm,Spraying thicker can result in spontaneous combustion and poor overall spray foam quality
- Internal temperature of installed pass must be 25ºC before installing subsequent passes Maximum thickness during 24h period is 203mm(8inches)
- Like most of foam product,foam made by SD1133is combustible,An thermal barrier must be installed in accordance with approved construction standards SD1133
- The service temperature of the foam with SD1133 is between -60~80ºC.
PACKING SPECIFICATION 220KGS/Drum, Blue paint or Zinc coating drums (Drum Weight: 18-23kg)
STORAGE RECOMMENDATIONS
The blend polyol should be stored in the sealed container to avoid the absorption of water vapor. During the transportation, it should avoid serious shake and strong sunlight. It should be stored in ventilated place, avoiding light, water and fire. Recommended storage temperature is 15~25ºC
.
Shelf life: 6 months, please test before using after 6 months storage.