Description of platinum cured silicone rubber
platinum cure silicone rubber is a kind of translucent liquid , generally named two-components silicone rubber with mixing in 1:1 .It’s mainly suitable for tire molds making .
Advantage of platinum cure silicone rubber for tire mold
Non- shrinkage
high tensile and tear strength with high copy times
exceptional fluidity and good operability (mixing ratio at 1:1)
high temperature resistant in 250 Centigrade
Operation instruction of platinum cure silicone rubber for tire mold
Step One: Take 100g of part A and 100g of part B and mix in 1:1 and mix the two part evenly.
Step Two: vacuum pumping
Without exception, this step takes less than 10 minutes.
Note: The time for vacuum-pumping should be less than 3-5minutes ,otherwise, once the silicone rubber has cross-link reaction during vacuum pumping process, it will not be operated.
Step Three: Pouring the mixture into the frame with original mold slowly .
Shelf life for silicon rubber for mold making
8~10months, when stored in a dry & cool place under the room temperature 25.
Packing for silicon rubber for mold making
20kg/drum for part A+ 20kg/drum for part B in one set
,200 kg/drum for part A+ 200kg/drum for part B in one set
For further information, pls contact with Miss ellar
TEL: 0086-755-89212365
Mobile: 0086-18938867558
Mail : hyxs(at)szrl(dot)net
Welcome to visit www (dot)szrl (dot)net anytime
https://www.facebook.com/mouldsilicone youtube:http://www.youtube.com/channel/UCed_-QO7UZneNYsWTxR1KFA>
linkedin:http://www.linkedin.com/profile/view?id=189510785&trk=nav_responsive_tab_profile_pic
twitter:https://twitter.com/Saminaray
you can try for rubber silicone rubber to get through more products
GA-90*1A/B series platinum catalyzed silicone mold making operates easily, A:B: mix evenly according to 1:1 ratio, product transparency is good, suitable for platinum vulcanization. The production of medical and health products needs to be treated by secondary vulcanization at ...
SiSiB® HR0100 is general purpose heat cured elastomer for molding. Technical Data Product HR0130 HR0140 HR0150 Appearance Translucent Translucent Translucent Hardness (Shore A) 30+/-2 40+/-2 50+/-2 Williams Plasticity 130+/-20 160+/-20 215+/-24 Tensile Strength (MPa) Min. 4.0 ...
Model Color Mixing ratio Pot life (mins) Demouled time (hrs) Hardness(A0) Tensile-strength (kgf/cm2) Tear-strength (kgf/cm) Viscosity (cps) Elongation (%) HY-E625 translucent 1 : 1 30-60 4±1 25±2 35±2 25±2 6000±3000 ≥400 HY-E630 translucent 1 : 1 30-60 4±1 30±2 40±2 ...