PA66 GF50(A2011J) for Engineering Plastics

PA66GF50 is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added to be used in injection molding products.

Typical Application of PA66 GF50 (A2011J)

PA 6.6 GF50 HB grade is applied to the field of industrial product structural parts, requiring high strength, high toughness, high and low-temperature resistance, and commonly used as water valve diverter and blade of air outlet, mechanical gears and bushings.

Other Details of PA6 6 GF50(A2011J)

Physical Property

Ash (50.0% 1 ISO3451/1)

Conditioned 600°C*2h

Density (1538Kg/m3 1 ISO1183)

Conditioned 23°C

Shrinkage Parallel Flow (0.1-0.3 % 1 ISO294-4)

Shrinkage Vertical Flow 0.2-0.5% I ISO294-4)

Mechanical Properties

Tensile strength (217.0MPa 1 ISO527)

Conditioned 5mm/ min

Tensile Strain at Break (2.5% I ISO527)

Conditioned 5mm/min

Notched Impact Strength (17.0KJ/m2 I ISO179

Conditioned 1.0J

Flexural Strength (354 MPa 1ISO178)

Conditioned 2mm/min

Flexural Modulus (14263 MPa I ISO178)

Conditioned 2mm/ min

Thermal Property

Melting Point (260°C I ISO11357)

Hot Deformation Temperature (260*C I ISO75)

Conditioned 1.8MPa

Flammability Class (HB 1UL94)

Conditioned mm

Injection Molding Conditions

Drying Temperature 130°C

Drying Time 3h

Cylinder Temperature 290-310°C

Nozzle Temperature 290-310*C

Tooling Temperature 80-100*C

* Molding conditions are just for reference, please make an adjustment based on the actual situation！

As an experienced plastic engineering inc and masterbatch factory, Anmei Group has a professional team of senior engineers with 10-15 years of R&D experience in engineering plastics and masterbatch, we work together to achieve our goal of solution providing and create more values for customers with our stable quality and professional technical service, making a better life for human beings.