PA6 GF30 Halogenated FR (A1014F) for Engineering Plastics

Minimum Order
1
Packaging
N/A
Delivery
15 Days

PA6 GF30 FR is a PA6 with 30% glass-fibers and halogens flame retardant.

PA 6 GF30 Halogenated FR Features

Glass fiber reinforced 30% PA66 PA6
Density(g/cm3) 1.12-1.14 1.38
Water absorption(%) 1.3-1.9 1
Surface hardness M100 M100
Shrinkage(%) 0.5 0.4
Continuous heat resistance 82-148 93-148
Heat distortion temperature(1.82MPa) 252 210
Heat distortion temperature(0.45MPa) 257 221
Tensile Strength/Mpa 151.7-175.4 89.2-172.4
Elongation(%) 3~5 5
Flexural yield strength/Mpa 282.2 123.7
Flexural modulus of elasticity/Mpa 8918.1 10340.1
Compressive strength/Mpa 202.6 131.4
Izod notched impact strength/(J/m) 117.1~138.7 160.1
Melting point/°C 264 220
Decomposition temperature/°C 360 320
Drying temperature/°C 100 100
Drying time/h 3~5 3~5
Injection temperature/°C 240~280 240~280
Mold temperature/°C 40~90 40~90

PA6 GF30 Plastic Halogenated FR Description
Halogen-free flame retardant nylon PA6 GF30 granule have the properties of low flame retardant density, low product shrinkage, excellent electrification performance, and less corrosion to molds.

- Flame retardant grade UL94-V0.

It meets glow-wire ignition temperature (GWIT) testing demands, recording as:

GWFI:750/3.0 (Note:750℃=725℃+25℃)

GWFI:850/3.0

-Compliant with ROHS standard

PA6 GF30 is used in connectors of baby stroller, auto parts, power tool housings and mechanical parts, etc.With the rapid development of new energy vehicles (including hybrid, pure electric and hydrogen energy), the automotive industry has an increasing demand for light weight, integration, miniaturization and electrification of auto parts. Nylon6 has a unique role and development prospects in the manufacture of integrated components for new energy vehicles.

PA6 GF30 halogenated FR (A1014F) Typical Application
PA6 GF30 flame retardant has achieved full coverage from electronic & electrical fields to the industrial, commodity consumer market, and even the automotive industry. Such as MCB panel (v0), power tool housing (HB), small household appliance accessories for bread machine housing and vacuum cleaner accessories (HB), and daily necessities structural parts-office chair legs (HB) and exhaust duct (HB), etc.

PA6 PA6 GF30 halogenated FR (A1014F) Other Details
Physical Property
Ash (15.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1250Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.5-0.7 % 1 ISO294-4)
Shrinkage Vertical Flow (0.7-1.1% I ISO294-4)
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527)
Conditioned 5mm/ min
Tensile Strain at Break (2.5% I ISO527)
Conditioned 1.0J
Notched Impact Strength (125 0MPa I ISO527)
Conditioned 2mm/min
Flexural Strength (190MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (5700 MPa I ISO178)
Conditioned 5mm/ min
Thermal Property
Melting Point (220°C I ISO11357)
Hot Deformation Temperature (175*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 240-260°C
Nozzle Temperature 240-260*C
Tooling Temperature 80*C
* Molding conditions are just for reference, please make an adjustment based on the actual situation!

If you want to know more about PA6 GF30 properties , please visit our website.

As one of masterbatch suppliers, we can offer sorts of related products for sale, is you have needs to buy masterbatch, please leave us a message.

  • Country: China (Mainland)
  • Business Type:
  • Market:
  • Founded Year:
  • Address:Qiushe Industrial Zone, Tongli Town, Wujiang District, Suzhou City
  • Contact:anmeiplastics .com
*Your name:
*Your Email:
*To:Suzhou Anmei Material Technology Co., Ltd
*Subject:
*Message:
Enter between 20 to 3,000 characters. English only.     Characters : 0 / 3000
*Enter the secure code shown below Mfrbee security Image      Reload Image

submiting now We do inquire for you , please wait ...

PA6 GF30 Heat Stabilized (A1006F, A1016F) for Engineering Plastics
PA6 GF30 Heat Stabilized (A1006F, A1016F) for Engineering Plastics

Anmei A1006F is a kind of material PA6 GF30, which is the injection grade resin by mixing the 30% glass fiber and heat stabilized polyamide 6. Typical Application of PA6 GF30 heat stabilized (A1006F) Injection reinforced grade PA6, containing 30% glass fiber, is with heat ...

Suzhou Anmei Material Technology Co., Ltd

Nylon66 PA66 Halogen-free FR (A2005X01) for Engineering Plastics
Nylon66 PA66 Halogen-free FR (A2005X01) for Engineering Plastics

Nylon66 PA66FR Halogen-free FR (A2005X01) for Engineering Plastics Flame-retardant PA66 is a halogen-free flame retardant engineering plastic made of nylon 66 resin as a base material (other fibers can also be added), mixed and extruded. Typical Application of Nylon66 PA66 ...

Suzhou Anmei Material Technology Co., Ltd

PA6 GF30 Halogen-free FR (A1015F) for Engineering Plastics
PA6 GF30 Halogen-free FR (A1015F) for Engineering Plastics

PA6 FR is a PA6 with 30% glass-fibers and flame retardant free of halogens. Typical Application of PA6 GF30 halogen-free FR (A1015F) PA 6 GF30 flame retardant free of halogens has achieved full coverage from electronic&electrical fields to the industrial, commodity consumer ...

Suzhou Anmei Material Technology Co., Ltd