1. RTV-2 Addition Cure Silicone Rubber for Cement Crafts Mold Making: flowable liquid silicon and catalyst.
2. RTV-2 Addition Cure Silicone Rubber for Cement Crafts Mold Making cures at room temperature within 3 hours.
Model | Color | Mixing ratio | Pot life (mins) | Demouled time (hrs) | Hardness(A0) | Tensile-strength (kgf/cm2) | Tear-strength (kgf/cm) | Viscosity (cps) | Elongation (%) |
E625 | translucent | 1 : 1 | 30-60 | 4±1 | 25±2 | 35±2 | 25±2 | 6000±3000 | ≥400 |
E630 | translucent | 1 : 1 | 30-60 | 4±1 | 30±2 | 40±2 | 23±2 | 7000±3000 | ≥395 |
E635 | translucent | 1 : 1 | 30-60 | 4±1 | 35±2 | 47±2 | 22±2 | 8000±3000 | ≥470 |
1. Step One: Take 100g of part A and add 100g of part B and mix the silicon rubber and the curing agent evenly.
2. Step Two: vacuum pumping
3. Without exception, this takes less than 10 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.
4. Step Three to useMolding Liquid Addition Cure Silicone Rubber: Brushing cast & Perfusion Molding operation.
Need any help on silicone rubber, please feel free to contact Ms Becky:
Tel:86-755-89212382
Mob/Whatsapp:86-18938867561
E-mail: hyjlyf(at)szrl(dot)net
Skype: Beckyliuting
SiSiB® HR0100 is general purpose heat cured elastomer for molding. Technical Data Product HR0130 HR0140 HR0150 Appearance Translucent Translucent Translucent Hardness (Shore A) 30+/-2 40+/-2 50+/-2 Williams Plasticity 130+/-20 160+/-20 215+/-24 Tensile Strength (MPa) Min. 4.0 ...
Model Color Mixing ratio Pot life (mins) Demouled time (hrs) Hardness(A0) Tensile-strength (kgf/cm2) Tear-strength (kgf/cm) Viscosity (cps) Elongation (%) HY-E625 translucent 1 : 1 30-60 4±1 25±2 35±2 25±2 6000±3000 ≥400 HY-E630 translucent 1 : 1 30-60 4±1 30±2 40±2 ...
Tin cured mould making liquid silicone rubber for sell Product Description 1.Description of Tin cured mould making liquid silicone rubber for sell It\'s a kind of room temperature vulcanized silicone rubber in condensation type. It’s generally named as two part silicone ...