Specification
- Durable
- High tear strength for replication
- Non-shrinkage
- High simulation
- Cover fine details
Unit Price: 9.76-13.58usd/kg
Model | E615 |
Appearance | Translucent |
Hardness(shore A) | 15±2 |
Mix ratio (A:B) | 1:1 |
Viscosity (mPa.s) | 8000±2000 |
Tensile-strength (MPa) | 4.2 |
Tear-strength (kN/m) | 12±2 |
Elongation (%) | 470 |
Density(g/cm3) | 1.05 |
Shrinkage rate(%) | 0.1 |
Pot life (mins) | 20-40 |
Curing time (hrs) | 3-5hrs(25℃) / 20-30mins(60℃) |
1. Please clean your original model(mother model) before you begin your mold making operation.
2.
Weigh suitable amount of E615 silicone.
3. Mixing the two parts by the ratio of 1:1/10:1 and mix part A and part B evenly in 2-3
minutes.
4. And get the mixture for vacuum-pumping for de-air the bubble in about 2-3 minutes.
5. Fix the mother model onto a clean wooden board.
5. Build a mold frame with four plastic plates or wooden plates, sealing the
gap.
6. Release agent should be applied onto the products’surface.
7. Pour the vacuumed
mixture into the model frame from the side of the mold frame.
8. When the silicone mixture gets cured, a clear silicone mold will come
out!
Need any help on silicone rubber, please feel free to contact Ms Lily:
Tel:86-755-89948294
Mob/Whatsapp:86-18938867596
E-mail:hyjz(at)szrl(dot)net
Skype:Lily941127@gmail.com
Food Grade Liquid Silicone Rubber SiSiB® LR1100 series are paste-like, easily pigmentable two-component liquid silicone rubber for injection molding process. Curing condition: Cure 10 minutes at 140oC, post cure 2 hours at 200oC. Application This liquid silicone product can be ...
Model Color Mixing ratio Pot life (mins) Demouled time (hrs) Hardness(A0) Tensile-strength (kgf/cm2) Tear-strength (kgf/cm) Viscosity (cps) Elongation (%) HY-E625 translucent 1 : 1 30-60 4±1 25±2 35±2 25±2 6000±3000 ≥400 HY-E630 translucent 1 : 1 30-60 4±1 30±2 40±2 ...
Specification of Non-toxic Food Grade Silicone Rubber for Sex Doll Non-toxic Food Grade Silicone Rubber for Sex Doll is generally named two-components siliconerubber, Part A and part B. It features an exceptional fluidity and good operability. The mixing ratio is 1:1, it ...