Seamless cold - finished tubes from Titanium Alloys

5,0 1,2 1,0-8,0 4,0 5,8 8,0 1,0 1,5 1,0-8,0 5,0 10,0 12,0 1,0 2,0 1,0-8,0 6,0 13,0 16,0 1,0 2,8 1,0-8,0 7,0 18,0 21,0 1,0 3,2 1,0-8,0 7,0 21 3,0 1,0-8,0 7,0 22,0 27,0 1,0 3,5 1,0-8,0 7,0 28,0 30,0 1,0 4,0 1,0-8,0 7,0 32,0 40,0 1,0 5,0 1,0-8,0 7,0 42,0 1,2 6,0 1,0-8,0 5,0 45,0 48,0 1,2 7,0 1,0-8,0 5,0 50,0 56,0 1,4 7,0 1,0-8,0 5,0 57,0 60,0 1,5 7,0 1,0-8,0 4,0 63,0 73,0 1,8 7,0 1,0-8,0 4,0 75,0 76,0 2,0 7,0 1,0-8,0 4,0 80,0 2,5 7,0 1,0-8,0 4,0 83,0 2,5 9,0 1,0-8,0 4,0 85,0 3,0 9,0 1,0-8,0 4,0 89,0 3,0 6,0 1,0-8,0 4,0 90-95 3,0-9,0 1,0-8,0 3,5 102-110 4,0-9,0 1,0-8,0 3,5 120 6,0-9,0 1,0-8,0 3,5 130 7,0-9,0 1,0-8,0 1,5 133 8,0-9,0 1,0-8,0 1,5 Due to agreement with Customer tubes can be delivered of intermediate sizes according to diameter and wall thickness. Chemical compositionAlloy grade Standard Chemical composition, % not more than Ti Al C Si Fe N O H Zr admixtures PT-1M OST 1 92077-91 base 0,2-0,7 0,07 0,10 0,20 0,04 0,12 0,007 0,30 0,30 PT-7M GOST 19807-91 base 1,8-2,5 0,10 0,12 0,25 0,04 0,15 0,007 2,0-3,0 0,30 27 OST 92077-91 base 3,0-4,2 0,10 0,12 0,25 0,04 0,15 0,007 2,0-3,0 0,30 In Alloy 27 Niobium and Vanadium content makes up in range for 0,7-1,5% for each. Hydrogen content is indicated according to requirements of standard to finished tubes. Mechanical propertiesAlloy grade At t 20

Tubes are produced seamless, cold-finished of titanium alloys PT-1M, PT-7M, 27.