cemented carbide parts

For rough machining and semi-fine machining abrasion resisting steel, manganese steel, stainless-steel, high-grade steel.

Having a higher strength, bearing a bigger shock capacity.

90.5

12.4-13.5

YW2

For machining abrasion resisting steel, manganese steel, stainless-steel, plain steel and cast-iron.

Having a higher hardness at high temperature, is a kind of universal hard metal.

91

13.0-13.3

YW1

For carbon steels fine turning and fine-boring.

Having higher wear-resistance and allowing faster cutting speed, the shock-resistance and vibration-resistance is worse.

92.8

9.3-59.7

YT30

For carbon steels semi-fine &fine turning, spiral turning, semi-fine &fine milling.

Having a worse vibration-resistance than YT14.

91

11.0-11.7

YT15

For continuous rough milling, cast-irons boring and rough boring.

Having a little worse vibration-resistance than YT5,but the wear-resistance is higher than YT5.

90.5

11.2-12.7

YT14

For machining of non-plain face for carbon steel and rough turning for incontinuous turning.

Having the best shock-resistance and vibration-resistance and the worse wear-resistance.

89.5

12.5-13.2

YT5

For making dies and cutters used under big shock and stress.

Having the highest strength and best shock-resistance.

89

13.4-13.5

YG20

For drawing and stamping dies.

The strength is higher than the above grades, but the wear-resistance is lower than the above grades.

87

13.9-14.1

YG15

For heavy rock drill bits.

Belonging the coarse tungsten
carbide, the strength is a little worse than YG15.

87

14.0-14.4

YG11C

For rough turning, planning, milling and electric drill bits.

Having higher strength, and the shock-resistance is better than YG6.

89

14.4-14.8

YG8

For machining cast-iron and thermal-resistance alloy, plain cast-iron, for making timber cutters.

Belonging the fine tungsten
carbide, having higher wear-resistance.

91

14.6-15.0

YG6X

For cast-iron, rough turning of threads, spiral turning and coarse & fine boring of holes.

Having higher wear-resistance, but lower than YG3X.

89.5

14.6-15.0

YG6

For the semi-fine machining of hard cast-iron & ferrous metal and alloy.

Belonging the fine tungsten
carbide, having more advantages than YG6X.

92

14.4-15.0

YA6

For geological prospecting, coal mining, tipping of electric and air drill  for coal bed.

Belonging the coarse tungsten carbide, the wear-resistance is higher than YG8S.

90

14.9-15.2

YG4C

For the drawing of cast-iron and fine wire, and the wear-resistance is superior.

Having the highest wear-resistance, but the toughness is the worst

92

 15.0-15.3

YG3X

Application

Properties

Hardness HRA

Density g/cm?

Grade

     have the consistent quality.
 4. Tungsten carbide parts we can supply for you as follows:
    -------die-set for cold punching & stamping      -------rectangular bar with different size
    -------HM round bar with different D &L            ------ tooth for all kinds of saw
    -------HM drawing die                                     -------sealing ring, wear-resistance parts
    -------heads for electric drills                           -------HM balls with different OD
    -------fabric parts, mechanic parts, nozzle etc. wear-resistance and re-abrasive parts

Introduction to tungsten carbide properties & application

           set, therefore to produce the needed tungsten carbide parts
  3. We have the strict quality control and assurance system to guarantee that our products  

            condition and requirements
      -------We will use different raw materials at different prices per your costing requirements
  2. We have the strong capability to design and make die-set
     -------For your non-standard parts, we are capable to design and make the required die- 

  1. Our tungsten carbide production starts from blending and milling
      -------We will select appropriate grade and composition for you per your application  

We could meet your requiements for grades and shapes &size of tungsten carbide parts what you need.