Polycarbonate Hard Coated Sheet

Note) The above figures are resulted in each test not absolute figures.

100/100

100/100

10%

Clear ink

JUJO

(general)

Color

test

Internal

100/100

100/100

10%

Clear ink

Seiko

(general)

Color

test

External

100/100

100/100

JA970 3%

Mirror ink

JUJO

(general)

Color

test

External

100/100

100/100

 3%

D Hardener

Mirror ink

Seiko

(general)

Color

test

External

100/100

100/100

NO2:NO3

Mirror ink

Seiko

(general)

Color

100/100

100/100

10%

C/gray

Seiko

Printing

1?C Back-

100/100

100/100

10%

JUJO AP black

(general)

Color

test

Internal

100/100

100/100

10%

Hark black

Seiko

(general)

Color

After 4 hours

during 40 min.

70/ after drying

Remark

Cross-Cut Test Result

Hardener

Ink Type

Type

Printing

5. Adhesive Promotion for Ink-Printing

No change

IPA

No change

Ethyl alcohol

No change

Methyl Alcohol

No change

10% Salt

No change

10% Alkali

No change

R.T  24H

10% Acid

Result

Testing-Standard

 

4. Chemical-Resistance Property

No problem

-3580 10cycles

Thermal-Shock Test

100/100

After 100-latticed & cross cutting with interval of 1 mm, 5 times

Using 3M cellophane adhesive tape

80 1H

of Heat-Resistance

Adhesive Force

No problem

120 1H

Heat-Resistance

100/100

After 100-latticed & cross cutting with interval of 1 mm, 5 times

Using 3M cellophane adhesive tape

Adhesive Force

Result

Testing-Standard

 

3. General Property

Excellent

Diameter 30mm

Bendability

Excellent

By reciprocating with 1kg Steel wool #0000 twenty times, measure the incidence of scratch

Anti-Scratch

HB~H

JIS-K5600

Test

Pencil Hardness

Result

Testing-Standard

 

2. Anti-Scratch Property

0.5% and less

Minolta CM 3600D

HAZE

90% and over

(430, 550, 630nm)

Minolta CM 3600D

(clear panel)

Transmission

Result

Testing-Standard

 

1. Optical Property

Physical Properties

Application
1. Protective Liquid-crystal windows of cellular phones
2. Name plates of all kinds of electronic devices