1.396g/cm3
ALCOHOL,23.0
Absolute
Method B
ASTM D792-00
Density
8
Pass
60+_5
63
Type A
17.99 mm
Thickness:
D2240-05
ASTM
Hardness
7
Pass
Max 40%
-2.4%
Change in elongation after heating aging
6
Pass
Max 15%
-2.4%
500mm/min
Die C Speed:
Specimen:
Method A
D412-98a(2002)
ASTM
Change in tensile strenght after heating aging
5
------
------
------
Time:70 Hours
Temperature: 100
ASTM C864-99
Heating aging
4
------
------
2.4Mpa
Tensile strength at 100% elongation
3
Pass
Min 250%
337%
Elonggation
2
Pass
Min 11.0 Mpa
11.2Mpa
500mm/min
Die C Speed:
Specimen:
Method A
D412-98a(2002)
ASTM
Tensile strength
1
Conclusion
Requirment
Test result
Test condition
Test Method
Test item
No. Over the years, PVC has been widely used in glass curtain walls due to its good properties and low cost. However, its heat aging resistance is poor compared with other rubber and thermoplastics. In our company, by adjusting the formulation, not only the heat aging resistance of PVC has been improved, but also hard-soft combined PVC sealing strips can be made according to the construct of glass curtain wall. PVC sealing strips for high-grade glass curtain wall |
PVC sealing strips for high-grade glass curtain wall
good qulity,good price,good severce
ISO 9000:2000 standard
Package: | According to customers'requirement |
Payment Terms: | L/C,T/T,Western Union,MoneyGram |
Port: | Shenzhen |
Standard or Nonstandard: | Nonstandard |
Shape: | Flat Gasket |
Material: | PVC |
Brand Name: | LHQ |
Place of Origin: | Guangdong China (Mainland) |