Its the non-dangerous goods, and it should be transported as the common chemicals.
Keep in dry place, the shelf time is nine months(Below 25)
7.Storage and Transportation:
Specification:40kg/set(A20 kgB20 kg); 400kg/setA200 kgB200 kg
6.Package:
5This product should be avoided being mixed with another kind of organic tin catalyst such as amines, sulfur, phosphorus compounds and some metal salts.Otherwise,the catalyst of this product will be useless that the mixed material will not be cured.
4Its non-dangerous goods.But pls dont have it touch mouth or eyes .If it happens,pls flushing yourself quickiy with enough rinsing.
3It has the connection for curing time to temperature of the material, the lower for the temperature,the longer for its curing time.
2The mixed material should be in sealed storage and be used up during the safety operation,or itll slowly cure to wastage
1 Mixing A&B compenent equably before using.
5.Precautions:
Injection molding:Put the mixed material which has been defoamed into the mold.The injection molding should be made under appropriate pressure,temperature , cycle and other conditions.
pumped when there is no bubble. Deaeration time is suggested to be 5 to 10 minutes or so.If there is no deaeration device,the next step can be proceeded when there is no foam in the mixed material,usually one hour after mixing.
Whipping: Adding B to vessel with A then mixing equably.
Defoaming:: Put the mixture in the vacuum deaeration device.Usually,it should not be
Measurement: Be exact Metage for A and B components.
4.Usage:
2.0
2.0
2.0
2.0
2.0
%
Linear Shrinkage
13
12
11
10
8
%
Tensile set
30
30
35
35
15
N/mm
Tear Strength
300
400
550
500
400
%
Elongation At Break
7.0
8.0
8.0
7.5
6
Mpa
Tensile Strength
70
60
50
40
30
ShoreA
Hardness
1.14
1.13
1.10
1.08
1.07
g/cm3
Gravity
700
500
300
70
50
Pa.S
Voiscosity
Semi-transparent
Semi-transparent
Semi-transparent
Semi-transparent
Semi-transparent
Exterior
Item
ADL3106-70
ADL3106-60
ADL3106-50
ADL3106-40
ADL3106-30
Unit
Property Model No. 3.Technical parameters:
ADL3106 serious has excellent elasticity and properties of anti-aging and resistence to high temperature afer curing under certain temperature(the temperature can be adjusted according to different demand).It has low linear shrinkage,resistence to impact fatigue,good thermal stability and cold resistence(the operating temperature is 60250).Below 20 ,the safe operating time in a sealed state after component A and B being mixed is 2 days.When the temperature becomes higher,the operating time will be shortened.
This product is high tensile injection mold RTV2 liquid silicone rubber.It is suitable for cook,orings, rubber covered roller,keypad, rubber wares and other silicone rubber products. 1.Application: ADL 3106 Injection Molding Silicone Rubber |
RTV2 liquid silicone rubber
high tensile
for injection mold
for cook,orings, rubber covered roller,keypad, rubber wares
Delivery Time: | within 10 days upon received payment |
Package: | 40kg/set(A20 kgB20 kg); 400kg/setA200 kgB200 kg |
Supply Ability: | 20 Ton per Week as contact |
Minimum Order Quantity: | 200 Kilogram as contact |
Payment Terms: | L/C,T/T,Western Union |
Port: | shenzhen |
exterior: | Semi-transparent |
hardness: | 30-70 |
Model Number: | ADL3106-30, 40, 50, 60, 70 |
Brand Name: | andalu |
Place of Origin: | Guangdong China (Mainland) |
Specification 1.Durable 2.High tear strength for replication 3.Low shrinkage 4.High simulation 5.Cover fine details Application hongyeliquid molding silicone rubberis suitable for industries such as toys, gifts, furniture decoration, construction decoration, stationery, ...
Packaging & Delivery Packaging Detail: 25kgs per drum or 200kgs per drum Delivery Detail: within 3 days after confirm of order Specifications liquid silicone rubber for mold making 2-component silicone with catalyst low viscosity easy operation good fluidity RTV-2 liquid ...
Come From 香港红叶节科技有限责任公司
Model Number:Hy528 Brand Name:HY silicone rubber Place of Origin:Zhejiang China (Mainland) with the resistance to deformation, good tensile strength as well as low shrinkage, and time of reproduction determined ...