large-scale sculpture duplication by liquid silicone rubber

FAX: 86 755 89948030

TEl: 86 755 89948013

if you need more information ,you can contact with Miss Ava,

The second reason is that the operator pour the silicone into the mold when the mixture is mixed evenly, then the finish silicone mold will not cure and dry entirely.

pattern or a unsmoothed surface, you should polish and clean the products after which it will be molded ,then spray the release agent. Normally, the release agent can be Vaseline , detergent. liquid wax Etc. In practical process, you can bush different release agent according to different material.

 The main reason for this problem is that you do not handle the products or original molds well, then you should deal with the original mold or products carefully before molding. Such as for the products with a complicated

 The solutions of the sticky of the silicone mold?

FAQs of the large-scale sculpture molds silicone rubber :

To mix the silicone and catalyst with a standard mixing ratio and then do the process of Vacuum-Pumping. Bubbles will come out during the mixing of the silicone and hardener, if without Vacuum-Pumping, the bubbles cannot be released from the mixture, as a result, there will be many bubbles in the finished silicone mold. Then the mold has a less tensile strength which will affect the reproduction times. Such an unsmoothed silicone mold will affect the quality of the production directly.

(3)Vacuum-Pumping Process

Firstly, you should deal carefully with the Original mold or the products you want to be molded. If no polishing of the Original mold or the products you want to be molded, the surface of the original mold or products is not so smooth or perfect, then the products made out of silicone molds will be not up to standard.

(2) Preparation of the Original molds

Component A is silicone rubber, and component B is curing agent or vulcanizing agent, usually the mixing ratio  will be 2-3%. Such as to 100G silicone rubber should be added 2G catalyst and then mix them totally(Note: the weight of the silicone and catalyst should be weighted correctly. According to local weather, the mixing ratio can be 100 to 2 under room-temperature 25 ⁰C; if the local weather is about 10 ⁰C, then the maximum mixing ratio should be 5%; When local temperature is -5 ⁰C, no reaction will happen between the silicone and hardener; once the temperature of local weather is 38-45 ⁰C, the mixing ratio of silicone and silicone rubber should be 1 %).

(1)  Correct mixing ratio

Operation Instruction forlarge-scale sculpture molds Silicone rubber:

Low shrinkage, no deformation, good elasticity, high duplication times, etc.

Features of large-scale sculpture molds silicone rubber:

      For large-scale sculpture molds duplication liquid silicone rubber  is also can be  applied for manual mold design, PVC plastic mould, cement product mold, low melting-point alloy mould, alloy toy crafts, plastic toy, craftwork, gift and stationery, big statue, cultural relic duplication,pad printing orientation, electronic appliances vibration resistance, etc.

Applications of large-scale sculpture molds silicone rubber:

mold silicone rubber is mainly used for model design of manual mold, huaman statue duplication