Above is the mixing data for silicon and curing agent, the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction, you are sure to manufacture first class products and maximize your profit this is not only the need of, but also our responsibility for and a satisfactory answer to our customers. We may not be the first, but we will try to be the best. The customers need is what we pursue!
(Note: curing agent can not be added above the 4% maximum level and the normal proportion is 2%. If more than 4% is applied, the silicon will condensate too fast for normal usage).
5.5. Curing agent reaction rate is related with weather and temperature. Under 25 degree, they can be added according to the instruction or at double amount in winter or under subzero temperature.
5.4. Added with 4% of curing agent, silicon can still flow within 10-15 minutes, mold can be released in 1-1.5 hours
5.3. Added with 3% of curing agent, silicon can still flow within 28-30 minutes, mold can be released in 1.5-2 hours
5.2. Added with 2% of curing agent, silicon can still flow within 50 minutes to 1 hour, mold can be released in 2-3 hours.
5.1. Added with 1% of curing agent, silicon can still flow within 2.5 hours, mold can be released in 6-8 hours.
5. Admixture amount of curing agent and silicon reaction:
4. Admixture amount of curing agent and chemical reaction of silicon: e.g., mix 100g of silicon with 50g of silicon oil, after they are sufficiently and evenly mixed, add curing agent as per 2% of the total weight of silicon and silicon oil, mix again for 2-3 minutes before exhausting. Generally exhausting duration can not exceed 10 minutes; otherwise, the silicon will harden quickly to affect the quality of molding.
3. The normal proportion is as follows: 100g silicon admixed with 30g silicon oil for a hardness of 20 A
silicone rubber:1) High reprint times.2) resonable price.3)all kind of color 4)Curing agent for free 5)Permanent and durable
Delivery Time: | 3days after we got your paid from our bank |
Package: | 20kg/pail 200kg/pail |
Supply Ability: | 20000 Kilogram per Day |
Minimum Order Quantity: | 200 Kilogram The best choice is 450kg.As it will save cost with you. |
Payment Terms: | L/C,T/T |
Port: | FOB SHEN ZHEN |
FOB Price: | US $7.58 - 19.28 |
color: | red.green.yellow.white |
Model Number: | 918# 2018# 900# |
Brand Name: | Hong Ye Silicone rubber |
Place of Origin: | Guangdong China (Mainland) |
Food Grade Liquid Silicone Rubber SiSiB® LR1100 series are paste-like, easily pigmentable two-component liquid silicone rubber for injection molding process. Curing condition: Cure 10 minutes at 140oC, post cure 2 hours at 200oC. Application This liquid silicone product can be ...
Come From Nanjing SiSiB Silicones Co., Ltd
Main Products:rapid prototype,3D printing,small volume production,CNC machining,vacuum casting, moulds making, injection production Business Type:Manufacturer, Trading Company Categories: Mechanical Parts & Fabrication Services ...
Come From Jierui Prototype Technology Co.,Ltd
1.Material and Hardness:LSR 55-60A fog face and transparent 2.Counterpart:/ 3.Packaging:/ Dongguan JuYan Silicone Technology Co.,Ltd (a BELLO company) is dedicated to offer high-quality rubber &silicone parts by integrating R&D,production,sales and service ,which are widely ...