BITUMEN

15.01.1997 - SUPPLY COMMITTEE

for SUPPLY COMMITTEE

SUPPLY COMMITTEE CHAIRMAN 35

EPPCO PRODUCT SPECIFICATION

.

SR.NO PROPERTIES

TEST METHOD

IP ASTM LIMITS REMARKS

1 DUCTILITY AT 25 DEG.C, cm - D113 MIN. 100

2 FLASH POINT, COC, DEG.C. 36 D92 MIN. 232

3 FOAM ON HEATING TO 175 DEG. C. - - NONE

M20-70

AASHTO(A)

NOTE (1)

4

100 g for 5 secs.

PENETRATION AT 25 DEG.C. 49 D5

MAX. 70

MIN. 60

5

MASS %

SOLUBILITY IN TRICHLOROETHYLENE, 47 D2042 MIN. 99.0

6

DUCTILITY OF RESIDUE AT 25 DEG.C., cm

ORIGINAL

RETAINED PENETRATION AS % OF

LOSS ON HEATING, MASS %

THIN-FILM OVEN TEST

45 D1754

MIN. 50

MIN. 54

MAX. 0.80

7 WATER, % VOL. 74 D95 NIL

8 DENSITY, RELATIVE AT 25/25 DEG.C. 189 D 70 REPORT

FOAMING SHALL CONSTITUTE FAILURE OF THIS TEST.

(1) TO BE OBSERVED WHEN CONDUCTING THE FLASH POINT DETERMINATION. ANY EVIDENCE OF

NOTE:

ASPHALT 60-70

EPPCO PRODUCT SPECIFICATION

REISSUE DATE SUPERSEDES ISSUE DATED ISSUED BY APPROVED BY : TAM PAGE NO.

15.01.1997 - SUPPLY COMMITTEE

for SUPPLY COMMITTEE

SUPPLY COMMITTEE CHAIRMAN 37

SR.NO. PROPERTIES

TEST METHOD

IP ASTM LIMITS REMARKS

1 DUCTILITY AT 25 DEG.C, cm - D113 MIN. 100

2 FLASH POINT, COC, DEG.C. 36 D92 MIN. 232

3 FOAM ON HEATING TO 175 DEG. C. - - NONE

M20-70

AASHTO(A)

NOTE (1)

4

100 g FOR 5 secs.

PENETRATION AT 25 DEG.C. 49 D5

MAX. 50

MIN. 40

5

%

SOLUBILITY IN TRICHLOROETHYLENE, MASS 47 D2042 MIN. 99.0

6

DUCTILITY OF RESIDUE AT 25 DEG.C., cm

RETAINED PENETRATION AS % OF ORIGINAL

LOSS ON HEATING, MASS %

THIN-FILM OVEN TEST

45 D1754

MIN.100

MIN. 58

MAX. 0.80

7 WATER, % VOL. 74 D95 NIL

8 DENSITY, RELATIVE AT 25/25 DEG.C. 189 D70 REPORT

FOAMING SHALL CONSTITUTE FAILURE OF THIS TEST.

(1) TO BE OBSERVED WHEN CONDUCTING THE FLASH POINT DETERMINATION. ANY EVIDENCE OF

NOTE:

ASPHALT 40-50

WE OFFER BEST QUALITY & HIGHLY RELIABLE PRODUCTS WITH A COMPETIOTIVE PRICE .
QUALITY IS ONE OF THE MAIN BENCHMARK WE FOLLOW