HS 2343ESR-S Hot Work Die Steel
Product Quick Detail
- Place Of Origin
- Jiangyin
- Minimum Order
- 1
- Packaging
- N/A
- Delivery
- 30-45day
Specifications
As large-size (thickness range 400-750mm) and high-polished plastic mold steel, HS 2343ESR-S, as a 1.2343 steel equivalent material, has higher purity and good structure uniformity through unique
smelting and heat treatment process.
The hot work steel has good polishing performance, good cold, and hot fatigue resistance and corrosion resistance, cold and hot processing performance, hardenability, as well as high thermal
strength, oxidation resistance, high toughness, and wear resistance at medium temperature.
HS 2343 ESR-S (1.2343 Material Steel Equivalent) Chemical Properties
Steel Grade C Si Mn P S Cr Mo V
HS 2343ESR-S 0.34-0.40 0.90-1.20 0.30-0.50 ≤0.014 ≤0.002 4.90-5.20 1.20-1.40 0.30-0.50
HS 2343 ESR-S (Material 1.2343 Equivalent) Applications
Plastic molds with a thickness of more than 400mm;
Auto lamp mold, automobile bumper, and dashboard mold, etc.
HS 2343 ESR-S (1.2343 Steel Equivalent Material) Features
Electroslag remelting, high-temperature diffusion annealing and ultra-fine heat treatment are applied, and make good structure uniformity and finely dispersed carbides;
Good heat and cold fatigue resistance and corrosion resistance, good cold and hot processing performance, high toughness and wear resistance;
High purity control brings high polishability;
High isotropy, aspect ratio ≥0.85;
Annealing hardness ≤200HB, quenching hardness 50-60HRC, tempering hardness 46-48HRC.
Material 1.2343 Steel Equivalent
HS 2343 ESR-S steel, which is a 1.2343 steel equivalent material, belongs to electroslag remelting hot work die steel. It has uniform microstructure, excellent machinability and polishability, high
toughness and high plasticity, high wear resistance, and overall hardening performance at high and low temperatures are both excellent. You can find 1.2343 steel equivalent to ASTM A681 H11 / ISO
4957 X37CrMoV5-1 / GB/T 1299 4Cr5MoSiV /JIS G4404SKD6 / FDAC from HITACHI
HS 2343 ESR-S (Material 1.2343 Equivalent) Heat Treatment
Soft Annealing:
820 to 860°C, after being heated through, cooling down to 600°C at a rate of 10°C/h with the furnace, then air-cooling, hardness max 230 HB.
Stress relief annealing: after rough machining, heating to 650℃ and holding for more than 2h, cooling down to 500℃ with the furnace, and then air cooling.
Quenching:
Preheating under a protective atmosphere to 500-600 ℃ for the first time, 820-860 ℃ for the second time, and finally heating to 900-1010 ℃
Quenching after being heated through at the quenching temperature for more than 30 minutes, hardness will be 50-55HRC.
Tempering:
Slowly heating to tempering temperature 560-600 °C after quenching, and it is recommended at least twice tempering. Achievable hardness: 42−50 HRC.
As a die steel supplier, we will do our best to meet all the needs of customers.
- Country: China (Mainland)
- Business Type:
- Market:
- Founded Year:
- Address:No.1 Dongmeng Rd,Dongmeng Technology Industrial Aggregation Area, Guanshan Village,Nanzha Street, Jiangyin,Jiangsu,China
- Contact:Echo Dai
Other products from Jiangsu Hongsheng Heavy Industry Group Co., Ltd
Relate products of HS 2343ESR-S Hot Work Die Steel
HOT WORK DIE STEEL
Hot work die steel, also known as hot work tool steel, is a type of steel specifically designed to withstand high temperatures and severe mechanical stress during hot forming processes such as forging, extrusion, and die casting. It is used to create and shape metal components ...
HS DVN/ HS DVN-Nb Hot Work Die Steel
As high-performance Cr-Mo-V hot work die steel, HS DVN / HS DVN-Nb steel has high high-temperature strength and thermal fatigue resistance, is widely used in casting dies, hot extrusion dies, hot punching dies, hot forging dies, etc. Chemical properties of HS DVN/ HS DVN-Nb ...