The Zero baking self-flow material adopts the selected high aluminum material (grade II) as aggregate which will be approximately processed into round particles.The bauxite cement shall be coagulant rather than binding agent and then combined with special comprehensive anchoring agent to achieve zero baking.Owing to its excellent flowability,this material is application to the urgent repair of the furnace water-cooled tube and other parts.After removing mould upon construction,this material is free of maintenance and baking and can be directly used after raising the temperature.When in use,it is free of falling and crack and shows high temperature performance superior to conventional self-flow material.
Physicochemical index for Zero baking self-flow material
item | index | |
Al2O3(%) :≥ | 55 | |
Volume density (g/cm3) :≥ | 2.1 | |
Rupture strength
(MPa) :≥ |
110℃×24h | 3 |
1250℃×3h | 6 | |
Compression strength (MPa):≥ | 110℃×24h | 20 |
1250℃×3h | 30 | |
Linear change rate (%) | 1250℃×3h | ±0.8 |
Maximum service temperature (℃) | 1300 | |
Baking duration (day) | 0 |
web:en.jznem.cn
email:jznem-sunny@hotmail.com
skype:122352056@qq.com
As one of the reliable refractory metal suppliers, Huasheng Metal are keeping a large and comprehensive inventory of the highest quality in form of types of refractory metals such as Powder, Bar, Rod, Sheet, Ingot, Wire and Block, etc., to ensure our customers with fast ...
Brown fused alumina is made of high-quality bauxite, anthracite, and iron filings. It is cooled and smelted at a high temperature by more than 2000 degrees in an electric arc. It is crushed and shaped by a jaw crusher and a ball mill. Description of Brown Fused Alumina for ...
As one of the reliable refractory metal suppliers, Huasheng Metal are keeping a large and comprehensive inventory of the highest quality in form of types of refractory metals such as Powder, Bar, Rod, Sheet, Ingot, Wire and Block, etc., to ensure our customers with fast ...