This series of hard-wearing mouldable material applies compact high alumina clinker as aggregate and meanwhile by adding aluminium oxide micro powder, silicon dioxide micro powder and high-efficiency compound bonding agent for mixing. The product needs no mixture during construction. This hard-wearing mouldable material is characterized by appropriate construction time, quick firing, great wear resistance, long service life, etc.
Main physicochemical index for Hard-weaing mouldable material
Item | KSL65 | KSL70 | KSL75 | |
Al2O3(%) :≥ | 70 | 70 | 75 | |
Volume density (g/cm3) :≥ | 2.3 | 2.4 | 2.5 | |
Compression strength (MPa):≥ | 110℃×24h | 60 | 65 | 65 |
1000℃×3h | 65 | 75 | 85 | |
Rupture strength
(MPa) :≥ |
110℃×24h | 8 | 8 | 9 |
1000℃×3h | 10 | 11 | 12 | |
Linear change rate (%) | 1000℃×3h | 0~-0.5 | 0~-0.5 | 0~-0.5 |
Heat shock resistance (times) :≥ | 900℃, water cooling | 25 | 25 | 25 |
Wearing capacity at normal temperature (cm3) :≤ | 900℃×3h | 6 | 6 | 5 |
Maximum service temperature (℃) | 20~40 |